Characteristics of tri-axial carbon fabric:

Carbon fiber triaxial fabric is a kind of high performance composite material ‌ has excellent mechanical properties and durability. ‌

The carbon fiber triaxial fabric is composed of ‌ the first fiber bundle, ‌ the second fiber bundle and the third fiber bundle. ‌ is braided along the three axes. ‌ forms the second hexagon element and a number of first hexagon elements connected in turn. ‌ compared with the common triaxial fabric, the crossing points of ‌ triaxial fabric are reduced, the fracture points of ‌ fiber are greatly reduced, ‌ is more beneficial to resin immersion and the strength of ‌ is increased. ‌ In addition, the application of ‌ carbon fiber triaxial fabric not only increases the tearing resistance, ‌ also reduces the bending degree of the fiber bundles, ‌ reduces the deformation, ‌ thus prolongs the service life. ‌ The unique structure of this material significantly improves the overall strength and stiffness, ‌ has good ablative resistance and damage resistance, ‌ is very suitable for high energy thermal structural functional materials. ‌

Carbon fiber triaxial fabric is widely used in ‌, including aviation, ‌ aerospace, ‌ military, ‌ automobile, ‌ medical and advanced sports server. ‌ The three-dimensional textile composite material has two characteristics of integrity and excellent mechanical structure. ‌ from weaving and ‌ composite to finished product, ‌ no stratification, ‌ no mechanical processing, ‌ or only a small amount of processing without operation of the fiber, ‌ to maintain the integrity of the product. ‌ The use of this material not only overcomes the disadvantages of low interlaminar shear strength and easy layering of traditional laminates fundamentally, ‌, but also significantly improves the mechanical properties of the composite in many aspects, ‌ makes it a new prospect in the field of composite materials

Parameters of tri-axial carbon fabric

Product	600gsm triaxial carbon fabric
Item	Unit	Result
Gram weight	g/m²	600
Width	mm	1270
Thickness	mm	0.9mm±0.09
Pattern		0/+45/-45
Fiber Density(0°)	/cm	2
Fiber Density(+45°)	/cm	5.5
Fiber Density(-45°)	/cm	5.5

Carbon fiber materials	K	12K, T400
Breaking strength	Mpa	4000-4500
Modulus	Gpa	>235