Product description:

350gsm ±45° T700 strength biaxial carbon fiber fabric has higher strength, lighter weight, and can withstand greater tension. It is an ideal choice for high tensile strength requirements.

- High strength: The tensile strength of T700 carbon fiber can reach about 4900MPa, which is higher than that of ordinary strength carbon fiber. The carbon fiber fabric made of it has high strength and can meet the needs of engineering or products with high strength requirements.

- Low density: The density is about 1.78g/cm³, which is much lower than that of metal materials. It can greatly reduce the weight of the structure. When used in aerospace, automobile and other fields, it is conducive to improving transportation efficiency and reducing energy consumption.

- Good flexibility: The diameter is about 5-7μm, which is thinner than hair. It can be made into products with complex shapes and structures. It is suitable for parts with special shape requirements, such as reinforcement of special-shaped structures and manufacturing of parts with complex shapes.

- High temperature and corrosion resistance: It has good high temperature resistance and corrosion resistance, can be used stably for a long time in harsh environments, and can be used in high temperature and high corrosion risk environments, such as chemical equipment, marine engineering and other fields.

Difference from ordinary strength biaxial carbon fiber fabric

- Strength: The tensile strength of ordinary strength biaxial carbon fiber fabric is usually below 4500MPa, while 350gsm ±45° T700 strength biaxial carbon fiber fabric has significantly higher strength and can be used in key parts with high load-bearing capacity requirements.

- Application scenarios: Ordinary strength is suitable for temporary structure reinforcement or repair and other scenes with low strength requirements; T700 strength is suitable for aerospace, automotive industry, sports equipment and other fields with high material performance requirements.

- Product performance: At the same weight, T700 strength carbon fiber fabric can provide higher strength and better mechanical properties, making the product lighter while maintaining or improving its performance and safety.

- Cost: T700 carbon fiber production process is complex, and has high requirements for raw materials and production equipment, resulting in higher costs, while ordinary strength carbon fiber fabrics are relatively low in cost.

Parameters of bi-axial carbon fabric

Product	350gsm biaxial carbon fabric
Item	Unit	Result
Gram weight	g/m²	350
Width	mm	1270
Thickness	mm	0.5mm±0.05
Pattern		+45/-45
Fiber Density(+45°)	/cm	5.3
Fiber Density(-45°)	/cm	5.3

Carbon fiber materials	K	12K, T700
Breaking strength	Mpa	>4900
Modulus	Gpa	>235